Groups | Count | Sum | Average | Variance | |||
< 75 μm | Melt 180 | 3 | 0.058 | 0.019 | 1.66E−05 | ||
Melt 200 | 3 | 0.089 | 0.029 | 2.59E−05 | |||
Melt 220 | 3 | 0.101 | 0.033 | 3.01E−06 | |||
75–106 μm | Melt 180 | 3 | 0.146 | 0.048 | 3.71E−05 | ||
Melt 200 | 3 | 0.185 | 0.061 | 2.93E−05 | |||
Melt 220 | 3 | 0.186 | 0.062 | 4.81E−05 | |||
106–150 μm | Melt 180 | 3 | 0.147 | 0.049 | 4.2E−05 | ||
Melt 200 | 3 | 0.182 | 0.060 | 2.09E−05 | |||
Melt 220 | 3 | 0.182 | 0.060 | 1.32E−05 | |||
Source of variation | SS | df | MS | F | p-value | F crit | |
< 75 mm | Between groups | 0.0003 | 2 | 1.65E−04 | 10.88 | 0.0101 | 5.143 |
Within groups | 0.0001 | 6 | 1.52E−05 | ||||
Total | 0.0004 | 8 | |||||
75–106 μm | Between groups | 0.0003 | 2 | 0.00016 | 4.39 | 0.066 | 5.143 |
Within groups | 0.0002 | 6 | 3.81E−05 | ||||
Total | 0.0005 | 8 | |||||
106–150 μm | Between groups | 0.0002 | 2 | 0.00013 | 5.39 | 0.045 | 5.143 |
Within groups | 0.0001 | 6 | 2.53E−05 | ||||
Total | 0.0004 | 8 |