From: Synthesis, stability, and emission analysis of magnetite nanoparticle-based biofuels
Precursors | Precipitating Agent | Reaction conditions | Particle Size (nm) | Ref |
---|---|---|---|---|
0.75g FeCl2 4H2O & 1.75g Fe(NO3)3 6H2O | 5.5 ml NH4OH | Stirring by 500 rpm | 13±1 | [65] |
1.625g FeCl2 4H2O & 4.430g FeCl3.6H2O | 10 ml NH4OH | Stirring by 1000 rpm for 2h at 25 °C |  | [66] |
10 & 20 mmol/L FeCl3 FeCl2 | 1 M NaOH | _ | 3 to 5 | [67] |
1:2 M FeCl2.4H2O & FeCl3.6H2O | NaOH | _ | 10.56 | [68] |
17.15g FeSO4·7H2O & 35.5 ml FeCl3 | 20.7g NaOH | _ | 10–50 | [69] |
25mM FeCl2& 50mM ferrous nitrate | NaOH, KOH, NH4OH | Stirring for 1 h at 25°C | 11.23±2.04 | [70] |
Stirring for 1 h at 50°C | 9.01±1.30 | |||
Stirring for 1 h at 70°C | 6.83±1.11 | |||
5.2g of FeCl3& 4.448g FeSO4·7H2O | 1.5 M NaOH | Stirring by 600 rpm at room temperature | 86.01 | [71] |
6.5g of FeCl3& 5.56g FeSO4.7H2O | 1.5 M NaOH | Stirring by 600 rpm with heating at 80 ÌŠC | 74.14 | |
1.99g FeCl2.4H20 & 5.41g FeCl3.6H2O | 25% NH3.H2O | Stirring at 25oC,40oC,60oC,80oC for 60 min | 10.14±0.2 10.32±0.9 10.95±0.8 11.66±0.87 | [72] |
FeCl2.4H2O & FeCl3.6H2O | 35 ml NaOH | stirring by 200 rpm at 25 °C | 10.03 | [73] |
FeCl2.4H2O & Fe2(SO4)3 | 6.6 | |||
FeCl2.4H2O & Fe(NO3)3.9H2O | 8.86 | |||
FeSO4.7H2O & FeCl3.6H2O | 8.7 | |||
FeSO4.7H2O & Fe2(SO4)3 | 5.1 | |||
FeSO4.7H2O & Fe(NO3)3.9H2O | 8.23 | |||
8.64g FeCl2 4H2O & 23.50g of FeCl3 6H2O | 34.4 ml NH4OH | Stirring by 300 rpm & heating at 60oC | 20-78 | [74] |
0.01M FeCl2∙4H2O & 0.02M FeCl3∙6H2O | 0.08-0.1 M NaOH | Stirring at 500 rpm | 10.7-11.5 | [75] |
0.09 KOH | 7.1 | |||
16.25g FeCl3& 6.35 g of FeCl2 | 2 M NaOH | Stirring at 30oC | _ | [76] |
1.5 g of FeCl2 4H2O & 3.0 g of FeCl3 | 10 ml NH4OH | Stirring at various temps. (0–90°C) | 10–40 | [77] |
2:1M FeCl2 4H2O & FeCl3·6H2O | 3M NaOH | Stirring for 30 min | 12.6-13.8 | [78] |
0.01 M FeCl2.4H2O & 0.02 M FeCl3.6H2O | 1.5M NaOH | _ | 10 to 13 | [79] |
1M (NH4)2Fe(SO4)2& 2M FeCl3 | 0.5M NaOH | Stirring & kept at 80oC | 20 | [80] |
1M FeCl2·4H2O and 2M FeCl3·6H2O | 20 ml NH4OH | Stirring by 300, 400, and 500 rpm | _ | [56] |